Method for formation of copper diffusion barrier film using aluminum

ABSTRACT

A method for formation of a copper diffusion barrier film using aluminum is disclosed. In the method, thin aluminum (Al) film is deposited on a dielectric, and a surface of the deposited aluminum film is plasma treated with NH 3 , thereby transforming the surface of the plasma treated aluminum film into a nitride film basically composed of aluminum nitride (AlxNy), and an aluminum film is deposited on the surface of the transformed aluminum nitride film, and copper is deposited on the surface of the deposited aluminum film. Therefore, because the diffusion of copper is suppressed, the problem that leakages between metal lines increase as pitches between the metals decrease due to high integrity of parts of semiconductor can be settled.

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The present invention relates to a method for formation of copper diffusion barrier film using aluminum, and more particularly to a method for formation of copper diffusion barrier film in a chemical-mechanical polishing (CMP) process, in which a thin aluminum film is deposited on a dielectric, the aluminum film is transformed into a nitride film basically composed of aluminum nitride (hereinafter, AlxNy), an aluminum film is deposited again on the transformed nitride film, and copper is deposited on the deposited aluminum film.

[0003] 2. Description of the Prior Art

[0004] As generally known in the art, in a CMP process, copper, which is one wiring material used in wiring semiconductor devices, is utilized as a metalization material which can reduce resistance-capacitance (RC) delay as its electric conductivity is low.

[0005]FIG. 1a and FIG. 1b are views showing conventional CMP process in which copper is deposited through electroplating.

[0006] As shown in FIGS. 1a and 1 b, copper is deposited through a Damascene process developed by IBM Inc., and is subjected to a CMP process. That is, a dielectric S1 pattern is formed on a substrate, then a copper diffusion barrier film S2 composed of titanium (Ti), titanium nitride (TiN), tantalum (Ta), tantalum nitride (TaN), etc., is formed on the dielectric pattern, copper S3 is deposited on the copper diffusion barrier film through electroplating, and the copper is then subjected to the CMP process.

[0007] However, because the diffusion coefficient of copper is high in almost all of the materials used in semiconductor fabrication, resulting in the deterioration of their transistor (TR) property, several kinds of diffusion barrier films have been developed and used in order to suppress the diffusion of copper.

[0008] Further, one more significant problem is that leakages between metal lines increase as pitches between the metals decrease, due to the high integrity of semiconductor devices.

SUMMARY OF THE INVENTION

[0009] Accordingly, the present invention has been made to solve the above-mentioned problems occurring in the prior art, and an object of the present invention is to provide a method for formation of copper diffusion barrier film using aluminum, in which a first aluminum film is deposited on a dielectric, a surface of the first aluminum film is transformed to a nitride film basically composed of aluminum nitride (AlxNy) by plasma treating the surface of the first deposited aluminum film with NH₃ or N₂, then a second aluminum film is deposited again on the transformed aluminum nitride film, and copper is deposited on the second deposited aluminum film.

[0010] In order to accomplish this object, there is provided a method for formation of copper diffusion barrier film using aluminum, the method comprising: a first step of depositing a first aluminum film on a dielectric; a second step of plasma treating the surface of the first deposited aluminum with NH₃, thereby transforming the plasma treated surface of the first aluminum film into a nitride film basically composed of aluminum nitride (AlxNy); a third step of depositing a second aluminum film on the transformed nitride film; and a fourth step of depositing a copper on the second aluminum film deposited.

BRIEF DESCRIPTION OF THE DRAWINGS

[0011] The above and other objects, features and advantages of the present invention will be more apparent from the following detailed description taken in conjunction with the accompanying drawings, in which:

[0012]FIGS. 1a and 1 b are views showing a conventional CMP process in which copper is deposited through electroplating; and

[0013]FIGS. 2a to 2 d are views showing a process for formation of copper diffusion barrier film using aluminum in a CMP process in accordance with the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0014] Hereinafter, a preferred embodiment of the present invention will be described with reference to the accompanying drawings.

[0015]FIG. 2a to FIG. 2d show a method for formation of copper diffusion barrier film using aluminum in a CMP process in accordance with the present invention. The method of the present invention comprises steps of: depositing a first aluminum film (Al) S4 on a dielectric S1, plasma treating a surface of the deposited aluminum film S4 with NH₃, thereby transforming the plasma treated surface of the first aluminum film S4 into a nitride film basically composed of aluminum nitride (AlxNy) S5, depositing a second aluminum film (Al) S6 on the transformed nitride film, and depositing copper (Cu) S8 on the second deposited aluminum film S6.

[0016] Based on the above-mentioned process, the method for formation of copper diffusion barrier film using aluminum according to the present invention will be described in more detail hereinafter.

[0017] As shown in FIG. 2a, a thin aluminum (Al) film S4 is firstly deposited on a dielectric S1. At this step, the aluminum film S4 is deposited through a sputtering method or a chemical vapor deposition method (CVD) and has a thickness of at most 100 Å.

[0018] Then, as shown in FIG. 2b, plasma treatment is performed with NH₃ on a surface of the first deposited aluminum film S4. The plasma treatment can be also performed on the deposited aluminum film S4 with N₂.

[0019] Subsequently, as shown in FIG. 2c, the plasma treated surface of the first aluminum film is transformed into a nitride film basically composed of aluminum nitride (AlxNy) S5, and then a second aluminum (Al) film S6 is again deposited on the transformed nitride film S5. At this step, the second aluminum film S6 is deposited through a sputtering method or a chemical vapor deposition method (CVD) and has a thickness of at most 100 Å.

[0020] Finally, as shown in FIG. 2d, copper (Cu) S7 is deposited on the second deposited aluminum film S6 in order to form a copper diffusion barrier film.

[0021] Therefore, as described above, the method according to the present invention comprises the steps of: depositing a first thin aluminum film on a dielectric, transforming the surface of the first deposited aluminum film into a nitride film basically composed of aluminum nitride (AlxNy) by plasma treatment with NH₃ or N₂, depositing a second aluminum film on the transformed aluminum nitride film, and depositing a copper on the second deposited aluminum film. Therefore, the method according to the present invention can suppress the diffusion of copper and prevent leakages due to the copper diffusion between metal lines from increasing according to the decrease of pitches between the metals as semiconductor devices are more highly integrated.

[0022] Although a preferred embodiment of the present invention has been described for illustrative purposes, those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims. 

What is claimed is:
 1. A method for formation of copper diffusion barrier film using aluminum, the method comprising: a first step of depositing a first aluminum film on a dielectric; a second step of plasma treating a surface of the first aluminum film with NH₃, thereby transforming the plasma treated surface of the first aluminum film into a nitride film basically composed of aluminum nitride (AlxNy); a third step of depositing a second aluminum film on the transformed nitride film; and a fourth step of depositing copper on the second aluminum film.
 2. A method for formation of copper diffusion barrier film using aluminum as claimed in claim 1, wherein the aluminum film is deposited through a sputtering method or a chemical vapor deposition method (CVD) and has a thickness of at most 100 Å.
 3. A method for formation of copper diffusion barrier film using aluminum as claimed in claim 1, wherein the surface of the aluminum film deposited in the first step is plasma-treated with N₂. 